Ruthenium Oxide Titanium Electrode Electrolytic Cell

ruthenium oxide titanium electrode electrolytic cell For water disinfection, metals recovery, removal of the cyanides and sulfides, electrochemical reduction, etc., electrochemical water treatment is used extensively.

Production process introduction
1、Purchase TA1 type titanium substrate to ensure the surface of the plate is flat and smooth without deep scratches and defects.
2、Process the selected titanium substrate into the size required by the customer.
3、Titanium substrate annealing and leveling temperature >500℃. (To reduce the pressure and ensure the flatness.)
4、Annealing and leveling treatment, the surface of titanium substrate will form a dense layer of titanium oxide, using mechanical or manual polishing, so that the titanium surface shows a metallic luster.
5、Acid washing with 10% concentration of oxalic acid to corrode the titanium substrate in a slightly boiling state for several hours to corrode the surface oxide layer to the hydrogenated titanium surface.
6、According to the anode environment used by the customer, the precious metal solution is configured in a reasonable qualitative and quantitative manner.
7, check whether the acid washing titanium substrate is qualified, that is, the surface layer is gray and uniform pockmarked structure, and then artificial coating, sintering at the appropriate temperature, sintering after natural cooling, secondary coating After cooling to room temperature. Application, and so on, until the application configuration solution more than 17 to 20 times.
8、After the above processed parts are sintered, a life test test is performed with the furnace test piece, and the test is packed and shipped

after passing.

Chlor-alkali industry test data.
1、Chlorine precipitation potential: ≤1.13v
2、Chlorine polarization rate: ≤40mv
3、Enhanced life: ≥3000min Current density 10000A/m2

our service:

1. Depending on the use environment, can deploy various coating formulations, better play electrocatalysis

2. Reduces precipitation chlorine overpotential, extends the service life of electrode, and is good resistant to corrosion.

3. Anode shape and size can be modified to suit the specific working conditions.

4. We can offer anode repair coating technology service based on the amount of anode coating consumed. The base material can be reused repeatedly without excessive loss

Packaging and shipping.
Tested and qualified products will be packaged in sponge foam or special cardboard boxes to prevent bumping or scratching, or we can package to your specific needs.

We will ship directly to your address using an international courier. We will ship within 48 hours, with an approximate courier time of 7-14 days.

The picture you see of the titanium anode is the same as the one you receive. If you have any questions during the purchase process or after you receive the product in the process of use, we will reply to you within 24 hours at the first time!

Customer Feedback:

why choose us:

Our quality director scrutinizes the offered ruthenium oxide titanium electrode electrolytic cell as per the pre-defined quality limits to provide a flawless range. These products have made our company acclaimed for its long shelf life and continuous operations.

Hot Tags: ruthenium oxide titanium electrode electrolytic cell, China ruthenium oxide titanium electrode electrolytic cell manufacturers, suppliers, factory, intex titanium electrode, titanium electrodes for electrolysis, Ir Ru Oxide Coated On Ti Anode 8 Micron, Ruthenium Oxide Coated Titanium Blades for Pool Salt Cell, Mixed Metal Oxide Ruthenium Iridium Titanium Electrode, mixed metal oxide electrode